| Model No.︰ | HBF601 |
| Brand Name︰ | HBWELD |
| Country of Origin︰ | China |
| Unit Price︰ | - |
| Minimum Order︰ | - |
|
|
|
|
|
Agglomerated Flux
HBF601
EQUALS TO EN760
Chemical compositions(%)
|
SiO2+TiO2
|
Al2O3+MnO
|
CaO+MgO
|
CaF2
|
S
|
P
|
|
5-10
|
30-40
|
6-10
|
40-50
|
0.06 Max
|
0.08 Max
|
Mechanical properties(Mpa)
|
With wire
|
Tensile Strength
|
Yield
Strength
|
Elongation
(%)
|
AKV(J)
|
|
-100 centigrade
|
|
ER309LMo
|
550-700Mpa
|
290Mpa Min
|
30% Min
|
47 Min
|
|
Inconel
|
550-700Mpa
|
290Mpa Min
|
30% Min
|
|
Melting metal analysis(%)
|
|
C
|
Si
|
Mn
|
Cr
|
Ni
|
Mo
|
S
|
P
|
|
ER309LMo
|
0.04 max
|
1.0 max
|
0.5-2.5
|
18-21
|
9-11
|
2-3
|
0.03
|
0.04
|
|
Inconel625
|
0.03
|
0.24
|
1
|
20
|
Bal
|
9
|
0.03
|
0.04
|
Flux type: aluminate-fluoride basic type
Basicity index: 1.8
Grain size:2.00-0.28mm(10-60meshes)
Description: The welded metal is very purity and shows excellent mechanical properties. The diffusible hydrogen content is less than 5ml/100g. It has excellent welding technology properties. Regularly shaped welds are deposited without reduction of area or interface notches. Slag detachability is good. It is suitable for submerged twin-wire, tandem and multi-wire welding as well as for welding with the two-run technique.The special production method ensures that the flux has low moisture pick-up and granular stability. Flux shall be capable of meeting the applied requirements.
Application: Joint welding of 18%Cr-12%Ni-2%Mo(309,316) stainless steels and surfacing of mild steels and low alloy steels. The low carbon stainless steels can be welded.
Package:25kg in one paper bag.
|
|
|
|
|
|
|
|