HBE308L-16
Accord to AWS E308L-16
The 0.04 percent maximum carbon content of weld metal deposited by HBE308L-16 reduces the possibility of intergranular carbide precipitation and thereby increases the resistance to intergranular corrosion without the use of stabilizers such as columbium (niobium) or titanium.
A carbon content of 0.04 percent maximum has been shown to be adequate in weld metal, even though it is
recognized that similar base metal specifications require a 0.03 percent limitation. This low carbon alloy.
Used for welding corrosion-resistant stainless steel
Chemical Analysis：%
|
|
C
|
Mn
|
Si
|
S
|
P
|
Cr
|
Ni
|
Mo
|
Cu
|
|
Typical
|
0.04
|
0.5-2.5
|
1.00
|
0.03
|
0.04
|
18-21
|
9-11
|
0.75
|
0.75
|
Mechanical Property
|
|
T.S
Rm(MPa)
|
Y.S
ReH(MPa)
|
Elongation
A(%)
|
Impact
AKV(J)
|
［H］ml/100g
|
|
Typical
|
520
|
-
|
35
|
-
|
-
|